直纺亮光抗倒伏波浪扁平涤纶FDY的开发

探讨了直纺83 dtex/114 f波浪扁平涤纶全拉伸丝(FDY)的工艺制备过程。试验证明,在熔体输送温度276~282℃,纺丝温度286~290℃,喷丝板规格DIO φ104 mm-114孔、"王"字形,环吹风压10~15 Pa,含油率1.1%~1.2%,卷绕速度3 800~4 200 m/min的工艺参数下纺制83 dtex/114 f波浪扁平涤纶FDY时,生产稳定,满卷率高,外观情况良好,袜带均匀亮丽,可批量生产。此新产品可用于制作高档布艺沙发表层面料,具有抗倒伏、色彩艳丽等功效。     

郴州某复杂硫化铅锌矿阶段磨浮试验研究

针对郴州某复杂硫化铅锌矿资源的性质特点,采用铅快速浮选后尾矿再磨再选的阶磨阶选工艺,较好地实现了铅锌的高效浮选回收。研究了磨矿方式、捕收剂和调整剂种类及用量等因素对该矿石浮选的影响,确定了最佳浮选条件,通过小型闭路浮选试验,得到了铅品位60.05%、回收率89.63%的铅精矿和锌品位47.01%、回收率88.14%的锌精矿。     

Highly Stretchable and Sensitive SBS/Graphene Composite Fiber for Strain Sensors

Flexible strain sensors have attracted tremendous interests due to the emergence of intelligent wearable technology. Electrically conductive fibers are desirable candidates for flexible strain sensors, but up til now, there still exist enormous challenges to obtain conductive fibers exhibiting simultaneously high stretchability and high strain sensitivity. This paper introduces a poly (styrene‐butadiene‐styrene) (SBS)/graphene (Gr) composite fiber‐based flexible strain sensor fabricated by a facile and highly scalable wet spinning method. The results demonstrate that the graphene content has significant influence on the morphology, mechanical properties, and electromechanical properties of the composite fibers. The fibers with 5 wt% graphene have a wide response range of up to 100% strain, a high electrical sensitivity with the gauge factor of 10083.98 at 100% strain, and meanwhile, a high level of stability for 2100 stretching–releasing cycles under an applied strain of 20%. Furthermore, the SBS‐5%Gr composite fibers display excellent sensing performance in detecting human upper limb movements at different joints including hand joints, wrist joints, elbow joints, and shoulder joints.     

Preparation of Al2O3-mullite thermal insulation materials with AlF3 and SiC as aids by microwave sintering

Al₂O₃-mullite composites were prepared under the synergy effect of AlF₃ and SiC aids by microwave heating. The phase composition, microstructure, porosity, flexural strength, thermal shock resistance, and thermal conductivity were investigated. The XRD results revealed that the content of mullite phase steadily increased with the increasing of AlF₃ content. The microstructure showed that the lower content (≤1 wt%) of AlF₃ led to the formation of granular mullite and the higher content (≥3 wt%) of AlF₃ led to the formation of mullite whiskers, which could form an interlocking structure. In addition, the SiC hot spots can also promote the generation of mullite whiskers by microwave sintering. The thermal shock resistance was significantly improved by the interlocking structure of mullite whiskers. The residual rate of flexural strength of the composite with 3 wt% AlF₃ was 86%. The composite with 3 wt% AlF₃ additives got its optimized thermal conductivity from 30°C to 950°C, the value was between 0.819 and 1.021 W/(mK), which possess excellent thermal insulation performance.     

喷射成形Al-Zn-Mg-Cu合金挤压态的组织和力学性能

研究了利用喷射成形辅以挤压制备Al-5.72Zn-2.36Mg-1.66Cu合金后优化的组织结构特征和力学性能。结果表明,合金基体组织均匀细化,晶粒形貌趋于圆整,平均晶粒大小达到10 μm左右。当合金的冷却条件通过快速凝固技术改变时,会产生不同程度的固溶强化效果和第二相弥散强化效果,从而改善了合金的整体性能。合金的屈服强度和抗拉强度分别平均提高了20%左右,且伸长率也略有提高。     

退火温度对0Cr25Al5热轧态盘条钢组织及性能的影响

采用显微组织分析和分子动力学模拟等方法研究了退火温度对0Cr25Al5热轧态盘条钢组织及性能的影响。结果发现,晶粒尺寸随温度的升高逐渐增加并趋于稳定,但是断后伸长率和断面收缩率在950 ℃突然大幅度下降。试样组织形貌在800 ℃和950 ℃退火温度下的OM及SEM分析结果未见明显差别。于是使用分子动力学模拟对0Cr25Al5钢三元体系的自由能进行了计算,发现随着B2结构的FeAl或者DO3结构的Fe₃Al有序相尺寸的增大,系统自由能先减小后增大,其最小值随着退火温度的升高向有序相颗粒尺寸减小的方向移动。在1273 K的高温下仍然会保留60 nm左右大小的有序相颗粒。因此,推测0Cr25Al5钢在大于950 ℃的温度范围内韧性下降是由于60 nm左右的B2结构的FeAl或者DO3结构的Fe₃Al有序相造成,与晶粒尺寸无关。因此,针对该钢种应进行低温退火促使基体组织回复以消除缺陷,从而抑制Fe、Al等基体原子的扩散。     

Formation of a protective layer against corrosion on Mg alloy via alkali pretreatment followed by vanillic acid treatment

Although Mg alloy possesses high specific strength, low density, and good biocompatibility, poor corrosion resistance hinders its further applications. In the present study, an innovative protective layer against corrosion was prepared on the AZ31 Mg alloy via alkali pretreatment followed by vanillic acid treatment. The alkali pretreatment supplied –OH for the AZ31 Mg alloy surface to react with vanillic acid. The vanillic acid treatment played a crucial role in enhancing the corrosion resistance due to the excellent ability to act as a barrier and retard aqueous solution penetration, which effectively isolated the underlying Mg alloy from the corrosive environment. The corrosion current density of alkali and vanillic acid-treated Mg alloy (AZ31V) almost showed two orders of magnitude lower values in comparison with that of the AZ31 Mg alloy, and the corrosion potential of AZ31V Mg alloy increased from −1.41 to −1.25 V. The immersion tests proved that there was no occurrence of severe corrosion. Hence, the alkali pretreatment and vanillic acid treatment may represent a promising method to improve the corrosion resistance of Mg alloy.     

Enhancing the intergranular corrosion resistance of high Mg-alloyed Al–Mg alloy by Y addition

Microalloying is thought to improve the performance of Al–Mg alloys commonly used in transport applications. The effect of Y addition (0–0.4%) on the microstructure, mechanical properties, and corrosion resistance of Al–9.2Mg–0.7Mn alloy is investigated for potential use in engineering applications. The generation of the β-Al₃Mg₂ phase along the grain boundaries is suppressed in the as-cast alloy due to the formation of the AlMgY ternary phase. The average intergranular corrosion mass loss of the alloy with 0.1% Y addition decreases about 53.1% almost at no expense of mechanical performance in the as-rolled alloy after annealing. Moreover, the alloy with 0.1% Y addition shows the corrosion mass loss about 30.2% lower than the Y-free alloy in the sensitized state. The enhanced corrosion resistance of the alloy can be ascribed to the reduced β-Al₃Mg₂ precipitation along the grain boundaries associated with Y addition.     

2.25Cr-1Mo与2.25Cr-1Mo-0.25V钢冷却转变对比分析

采用相变仪、光学显微镜及扫描电镜研究了2.25Cr-1Mo和2.25Cr-1Mo-0.25V钢冷却转变过程,并分析了钒对其冷却转变的影响。结果表明,与2.25Cr-1Mo钢的CCT曲线相比,2.25Cr-1Mo-0.25V钢铁素体转变区及贝氏体转变区均向右移,并且在现有试验条件下已无法观察到珠光体转变区;钒添加到2.25Cr-1Mo钢中,能够提高钢的淬透性,2.25Cr-1Mo-0.25V钢在48 000 ℃/h冷速下能生成部分马氏体;钒能够细化钢板显微组织,与2.25Cr-1Mo钢相比,2.25Cr-1Mo-0.25V钢在800 ℃/h冷速下组织更为细小。